[Influence of carbodiimide-ethanol solution surface treatment on dentin microtensile bond strength].
Zhang, Y, Liu, YH, Zhou, YS, Chung, KH
Beijing da xue xue bao. Yi xue ban = Journal of Peking University. Health sciences. 2015;(5):825-8
Abstract
OBJECTIVE To evaluate the microtensile bond strength changes and patterns of fractures of the bonding interface after dentine surface treatment with carbodiimide-ethanol solution. METHODS 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC) dissolved in ethanol was diluted into different concentrations of 2, 1, 0.3, 0.1 and 0.01 mol/L EDC-ethanol solutions. Twenty-eight caries-free extracted human third molars were ground metallurgically to prepare flat occlusal mid-coronal dentin surfaces and etched with 35% (mass fraction) phosphoric acid gel. Then they were treated with EDC-ethanol solution for 60 s before the bonding procedure and randomly divided into five experimental groups corresponding to the tested EDC-ethanol concentrations. The ethanol treated and no pre-treated surfaces were used as controls. Single Bond 2 adhesive was applied and resin composite disk was stacked on the treated dentine surface. The teeth with resin composite disks were stored in water at room temperature for 24 h and then sectioned longitudinally to produce stick specimens for microtensile bond strength test. Fracture patterns were observed with a stereomicroscope. RESULTS The dentin surfaces pre-treated with 2 mol/L [(22.17±13.31) MPa] and 1 mol/L [(45.31±17.80) MPa] EDC-ethanol solutions resulted in statistically significant lower bond strength value (P<0.05). Increasing numbers of fracture pattern at the resin-dentin interface were also found in this two groups with percentages of 81.2% and 41.3% respectively. No significant difference was observed in the groups with 0.3, 0.1, 0.01 mol/L EDC surface treatment (P>0.05). CONCLUSION No significant difference of immediate bond strengths was found in the 0.3, 0.1, 0.01 mol/L groups compared with the control group. EDC-ethanol solution surface treatment with concentrations of 2 mol/L and 1 mol/L resulted in decreasing of the bonding strength.